Titel: Plasma Treatments and Light Extraction from Fluorinated CVD-Grown (400) Single Crystal Diamond Nanopillars
VerfasserIn: Radtke, Mariusz
Slablab, Abdallah
Van Vlierberghe, Sandra
Lin, Chao-Nan
Lu, Ying-Jie
Shan, Chong-Xin
Sprache: Englisch
In:
Titel: C
Bandnummer: 6
Heft: 2
Verlag/Plattform: MDPI
Erscheinungsjahr: 2020
Freie Schlagwörter: single crystal diamond
nitrogen vacancies
nanofabrication
DDC-Sachgruppe: 500 Naturwissenschaften
530 Physik
600 Technik
Dokumenttyp: Journalartikel / Zeitschriftenartikel
Abstract: We investigate the possibilities to realize light extraction from single crystal diamond (SCD) nanopillars. This was achieved by dedicated 519 nm laser-induced spin-state initiation of negatively charged nitrogen vacancies (NV−). We focus on the naturally-generated by chemical vapor deposition (CVD) growth of NV−. Applied diamond was neither implanted with 14N+ , nor was the CVD synthesized SCD annealed. To investigate the possibility of light extraction by the utilization of NV−’s bright photoluminescence at room temperature and ambient conditions with the waveguiding effect, we have performed a top-down nanofabrication of SCD by electron beam lithography (EBL) and dry inductively-coupled plasma/reactive ion etching (ICP-RIE) to generate light focusing nanopillars. In addition, we have fluorinated the diamond’s surface by dedicated 0 V SF6 ICP plasma. Light extraction and spin manipulations were performed with photoluminescence (PL) spectroscopy and optically detected magnetic resonance (ODMR) at room temperature. We have observed a remarkable effect based on the selective 0 V SF6 plasma etching and surprisingly, in contrast to literature findings, deactivation of NV− centers. We discuss the possible deactivation mechanism in detail.
DOI der Erstveröffentlichung: 10.3390/c6020037
Link zu diesem Datensatz: urn:nbn:de:bsz:291--ds-313442
hdl:20.500.11880/30299
http://dx.doi.org/10.22028/D291-31344
ISSN: 2311-5629
Datum des Eintrags: 23-Dez-2020
Fakultät: NT - Naturwissenschaftlich- Technische Fakultät
Fachrichtung: NT - Physik
Professur: NT - Keiner Professur zugeordnet
Sammlung:SciDok - Der Wissenschaftsserver der Universität des Saarlandes



Diese Ressource wurde unter folgender Copyright-Bestimmung veröffentlicht: Lizenz von Creative Commons Creative Commons