Title: Aqueous wet coatings for transparent plastic glazing
Author(s): Winkler, Ralf-Peter
Schirra, Hermann
Sepeur, Stefan
Wegner, Iris
Schmidt, Helmut K.
Arpac, Ertugrul
Language: English
Year of Publication: 1999
OPUS Source: Thin solid films. - 351. 1999, 1/2, S. 209-211
SWD key words: Silane
Aluminium oxydatum
DDC notations: 620 Engineering and machine engineering
Publikation type: Journal Article
Abstract: Electrostatically stabilized particulate sols, e.g. aqueous silica or alumina sols, have been surface-modified to reduce the particle/particle interaction and to obtain electrosterically stabilized sols. Epoxy functionalized alkoxysilanes were used as surface modifiers for alumina, silica or zirconia particles to achieve water dispersible nanoparticulate coating materials. After evaporating the organic solvent (produced by hydrolysis and condensation) aqueous sol-gel coatings have been prepared with organic solvent contents below 5%. The storage stability of these materials has been investigated by Si-29-NMR. An amino functionalized alkoxysilane was used as condensation catalyst and the nanocomposite material was thermally cured at 130 degrees C after flow or spray coating on pretreated polycarbonate substrates. The coatings show excellent adhesion which was shown by cross cut and tape test. After 1000 cycles Taber abrasion test (CS-10F, 500 g, DIN 52347) losses of transmittance due to scattering of 2-6% were achieved with a coating thickness of about 5 µm.
Link to this record: urn:nbn:de:bsz:291-scidok-29622
Date of registration: 1-Sep-2010
Faculty: SE - Sonstige Einrichtungen
Department: SE - INM Leibniz-Institut für Neue Materialien
SciDok - Der Wissenschaftsserver der Universität des Saarlandes

Files for this record:
File Description SizeFormat 
sm199937.pdf141,69 kBAdobe PDFView/Open

Items in SciDok are protected by copyright, with all rights reserved, unless otherwise indicated.