Titel: Preparation of conducting ultrafiltration membranes from redispersable, nanoscaled, crystalline SNO2:Sb particles
Verfasser: Goebbert, Christian
Burgard, Detlef
Nass, Rüdiger
Aegerter, Michel A.
Schmidt, Helmut K.
Sprache: Englisch
Erscheinungsjahr: 1999
Quelle: Ceramics - getting into the 2000's / ed. by P. Vincenzini. — Part D. - Faenza : Techna, 1999. — (Advances in science and technology ; 16), S. 441-448
SWD-Schlagwörter: Nanopartikel
Ultrafiltration
Biomembran
Kompositmembran
Membran
Sol-Gel-Verfahren
Trennverfahren
Wässrige Lösung
DDC-Sachgruppe: 620 Ingenieurwissenschaften und Maschinenbau
Dokumentart : InProceedings (Aufsatz / Paper einer Konferenz etc.)
Kurzfassung: Inorganic membranes prepared by the sol gel method are promising for use as filter in separation processes. Unsupported and supported conducting membranes have been produced from redispersable nanoscaled crystalline Sb-doped SnO2 powders with a Sb content up to 5 mole % (with respect to Sn). The crystalline particles are monosized (~4 nm) and fully redispersable in aqueous solution at pH >= 8 with a solid content up to 36.8 vol%. By thermal treatment at different temperatures and times, the pore size diameter of the material can be adjusted from 4 to 20 nm with a very narrow pore size distribution (~ +-1 nm) and a total porosity of 63%, practically independent of the sintering parameters. Uniaxial compacted unsupported membranes present similar characteristics with however larger pore size distribution (+-5 nm) and 80% total porosity. Their electrical resistance decreases with sintering temperature and time down to 4 Omega (800°C, 8 h). Fully dispersed aqueous solutions of the powder (7,8 vol%) were used to prepare transparent conducting porous coatings on glass or ceramics by spin-coating. AFter thermal treatment (1 hour at 550°C) single layers 200 nm thick have a typical specific electrical resistance p=2.5-10-² Omega cm and an optical transmission in the visible range measured against air of 90%.
Link zu diesem Datensatz: urn:nbn:de:bsz:291-scidok-29554
hdl:20.500.11880/24696
http://dx.doi.org/10.22028/D291-24640
ISBN der Druckausgabe: 88-86538-17-0
SciDok-Publikation: 1-Sep-2010
Fakultät: Sonstige Einrichtungen
Fachrichtung: SE - INM Leibniz-Institut für Neue Materialien
Fakultät / Institution:INM
SE - Sonstige Einrichtungen

Dateien zu dieser Ressource:
Datei Beschreibung GrößeFormat 
sm199931.pdf2,99 MBAdobe PDFÖffnen/Anzeigen


Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.