Titel: Enhancement of fracture strength of cutted plate glass by the application of SiO2 sol-gel coatings
Verfasser: Endres, Klaus
Mennig, Martin
Amlung, Martin
Gier, Andreas
Schmidt, Helmut K.
Sprache: Englisch
Erscheinungsjahr: 1999
Quelle: High-performance coatings for transparent systems in large-area and, or high-volume applications : September 6 - 10, 1998 / 2nd International Conference on Coatings on Glass, ICCG. [H. Pulker ..., ed.]. - Amsterdam : Elsevier, 1999, S. 204-208
SWD-Schlagwörter: Glasscheibe
Glas
Biegefestigkeit
Sol-Gel-Verfahren
Rasterelektronenmikroskop
Tetraethylsilicat <Tetraethylorthosilicat>
DDC-Sachgruppe: 620 Ingenieurwissenschaften und Maschinenbau
Dokumentart : InProceedings (Aufsatz / Paper einer Konferenz etc.)
Kurzfassung: The influence of SiO2 sol-gel coatings on the bending strength of soda lime plate glass samples has been investigated by 3 point bending and double ring bending strength measurements. The samples were prepared by manual glass cutting and were coated with two different types of SiO2 coating: A TEOS coating (thickness of about 100 nm) was obtained from sols synthesized by acid catalysis of tetraethoxysilane and a MTKS coating (thickness of about 1 &micro;m) was obtained from a methyl modified nanoparticulate SiO2 sol. The coatings were applied by dipping and were densified at 500'°C for 1 h. The fracture strength &sigma;0 of edge coated plate glass (60 X 25 X 3.8 mm), determined by 3 point bending test (according to EN 843-1), was increased after coating with TEOS from &sigma;0 = 24 MPa to 40 MPa (67% increase). The fracture strength increased to &sigma;0 = 56 MPa (133% increase) on applying MTKS or a double coating of TEOS followed by MTKS. The evaluation of these measurements using Weibull statistical analysis resulted in m values of 4.1 and 4.2 for the TEOS and MTKS coating and 3.5 for double coating (uncoated glasses m = 5.7), respectively. These results combined with high resolution secondary electron microscopy investigations led to the conclusion that the strengthening effect of the two different sol-gel systems is due to a partial flaw healing and clamping of the crack sides.
Link zu diesem Datensatz: urn:nbn:de:bsz:291-scidok-29328
hdl:20.500.11880/24680
http://dx.doi.org/10.22028/D291-24624
ISBN der Druckausgabe: 0-444-50247-5
SciDok-Publikation: 9-Jul-2010
Fakultät: Sonstige Einrichtungen
Fachrichtung: SE - INM Leibniz-Institut für Neue Materialien
Fakultät / Institution:INM
SE - Sonstige Einrichtungen

Dateien zu dieser Ressource:
Datei Beschreibung GrößeFormat 
sm199915.pdf2,48 MBAdobe PDFÖffnen/Anzeigen


Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.