Titel: Hydrothermal synthesis of nanosize alpha-Al2O3 from seeded aluminum hydroxide
Verfasser: Sharma, Pramod K.
Burgard, Detlef
Nass, Rüdiger
Schmidt, Helmut K.
Jilavi, Mohammad H.
Sprache: Englisch
Erscheinungsjahr: 1998
Quelle: Journal of the American Ceramic Society. - 81. 1998, 10, S. 2732-2734
SWD-Schlagwörter: Hydroxide
Aluminium oxydatum
Böhmit
Röntgendiffraktometrie
DDC-Sachgruppe: 620 Ingenieurwissenschaften und Maschinenbau
Dokumentart : Journalartikel
Kurzfassung: α-Alumina and boehmite particles were synthesized by co-precipitation followed by a hydrothermal treatment. X-ray diffraction (XRD) indicated that α-Al2O3 was the major phase and coexisted with 4% of boehmite in the presence of the α-Al2O3 seeds. On the other hand, a single boehmite phase was obtained in the absence of the α-Al2O3 seed particles. The powder densified in the temperature range from 1050° to 1350°C. High-resolution transmission electron microscopy (HRTEM) showed that the particle size of the synthesized α-Al2O3 was 60 nm. The surface area was 245 m2/g.
Link zu diesem Datensatz: urn:nbn:de:bsz:291-scidok-28899
hdl:20.500.11880/24638
http://dx.doi.org/10.22028/D291-24582
SciDok-Publikation: 11-Jun-2010
Fakultät: Sonstige Einrichtungen
Fachrichtung: SE - INM Leibniz-Institut für Neue Materialien
Fakultät / Institution:INM
SE - Sonstige Einrichtungen

Dateien zu dieser Ressource:
Datei Beschreibung GrößeFormat 
sm199807.pdf71,77 kBAdobe PDFÖffnen/Anzeigen


Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.