Titel: Preparation of Al2O3/SiC nanocomposites with in-situ formed SiC
Verfasser: Hopf, Jürgen
Aslan, Mesut
Schmidt, Helmut K.
Sprache: Englisch
Erscheinungsjahr: 2006
Quelle: Ceramic forum international. - 83. 2006, 4, S. E39-E44
SWD-Schlagwörter: Nanokomposit
Pulver
Keramikpulver
Calcinieren
Heißpressen
DDC-Sachgruppe: 620 Ingenieurwissenschaften und Maschinenbau
Dokumentart : Journalartikel
Kurzfassung: Powder mixtures containing Al2O3, SiO2 and carbon black were calcined at 1625°C to form nanoscaled SiC within Al2O3 by means of the carbothermal reduction of SiO2. The prepared powders contained 5 and 10 vol. % SiC. These powders were densified by hot pressing, and composite ceramics with densities up to 99 % obtained. Microstructural analyses of the hot-pressed composites showed a monogeneous distribution of SiC particles with a particle size mainly under 100 nm. The fracture mode was intragranular. The fracture toughness determined by the ICL method using the Niihara approach for Palmqvist cracks was in the range of 5 MPa-m0,5. The fracture strength determined in a four-point bending test was around 540 MPa for the hot-pressed samples and around 630 MPa for the hot-pressed and postannealed samples.
Link zu diesem Datensatz: urn:nbn:de:bsz:291-scidok-31039
hdl:20.500.11880/24590
http://dx.doi.org/10.22028/D291-24534
SciDok-Publikation: 3-Mai-2010
Fakultät: Sonstige Einrichtungen
Fakultät 8 - Naturwissenschaftlich-Technische Fakultät III
Fachrichtung: SE - INM Leibniz-Institut für Neue Materialien
NT - Materialwissenschaft und Werkstofftechnik
Ehemalige Fachrichtung: bis SS 2016: Fachrichtung 8.4 - Werkstoffwissenschaften
Fakultät / Institution:INM
SE - Sonstige Einrichtungen

Dateien zu dieser Ressource:
Datei Beschreibung GrößeFormat 
sm200602.pdf6,68 MBAdobe PDFÖffnen/Anzeigen


Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.