Titel: Effect of heat treatment and additives on the photochromic and mechanical properties of sol-gel derived photochromic coatings containing spirooxazine
Verfasser: Hou, Lisong
Hoffmann, Bernd
Schmidt, Helmut K.
Mennig, Martin
Sprache: Englisch
Erscheinungsjahr: 1997
Quelle: Journal of sol gel science and technology. - 8. 1997, 1/3, S. 923-926
SWD-Schlagwörter: Mechanische Eigenschaft
Photochromie
Sol-Gel-Verfahren
Spirooxazine
Temperatur
DDC-Sachgruppe: 620 Ingenieurwissenschaften und Maschinenbau
Dokumentart : Journalartikel
Kurzfassung: The experimental results on the photochromic and mechanical properties of coatings containing 1,3-dihydro-1,3,3-trimethylspiro[2H-indole-2,3''(3H)-naphth(2,1-b)(1,4) oxazine] (SO) derived from 3-glycidyl-oxypropyltrimethoxysilane (GPTMS), bisphenol A (BPA) and 1-methylimidazole (MI) by sol-gel processing are presented. It is shown that heat treatment temperature is a conflicting factor to the photochromic intensity (ΔA0), photostability and abrasion resistance of the photochromic coatings. With increasing densification temperature the matrix rigidity increases leading to a decrease of ΔA0 and at the same time an enhancement of both abrasion resistance and photostability, the optimum heat treatment temperature is 110'°C under our experimental conditions. By the use of certain additives, e.g., fluorosilanes (FAS), not only ΔA0 but also the photostability and the abrasion resistance of the photochromic coatings have been further improved.
Link zu diesem Datensatz: urn:nbn:de:bsz:291-scidok-28337
hdl:20.500.11880/24574
http://dx.doi.org/10.22028/D291-24518
SciDok-Publikation: 19-Apr-2010
Fakultät: Sonstige Einrichtungen
Fachrichtung: SE - INM Leibniz-Institut für Neue Materialien
Fakultät / Institution:INM
INM
SE - Sonstige Einrichtungen

Dateien zu dieser Ressource:
Datei Beschreibung GrößeFormat 
sm199703.pdf254,26 kBAdobe PDFÖffnen/Anzeigen


Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.