Titel: Microstructural development and mechanical properties of pressureless sintered Al2O3/SiC composites
Verfasser: Aslan, Mesut
Dörr, Christian
Nass, Rüdiger
Schmidt, Helmut K.
Sprache: Englisch
Erscheinungsjahr: 1995
Quelle: Ceramic processing science and technology / ed. by Hans Hausner ... - Westerville, Ohio : American Ceramic Society, 1995. — (Ceramic transactions ; 51), S. 665-669
SWD-Schlagwörter: Druckloses Sintern
Mikrostruktur
Mechanische Eigenschaft
Silane
DDC-Sachgruppe: 620 Ingenieurwissenschaften und Maschinenbau
Dokumentart : InProceedings (Aufsatz / Paper einer Konferenz etc.)
Kurzfassung: Al2O3 green bodies containing 5 vol% SiC were prepared by slip coating. In order to obtain stable slips, the zeta potential of the SiC was adapted by chemical modificaiton of the surface using functional silanes (e.g. amino ethyl amino propyltrimethoxysilane). Another route for the preparation of homogeneous slips was developed by heterocoagulation of Al2O3 and SiC under well controlled pH conditions and by stabilizing of the heterocoagulated system with a non-ionic surfactant. Both routes led to homogeneous aqueous slips which could be slip-casted to green compacts with densities around 60% of theory showing an excellent distribution of the SiC within the Al2O3 matrix. Green compacts were pressureless sintered at 1800°C to densities above 98.5% showing a homogeneous microstructure with average grain sizes between 2 and 2.5 µm, a fracture strength of about 650 MPa and fracture toughness around 3.0 MPa m0.5.
Link zu diesem Datensatz: urn:nbn:de:bsz:291-scidok-27991
hdl:20.500.11880/24545
http://dx.doi.org/10.22028/D291-24489
ISBN der Druckausgabe: 0-944904-89-0
SciDok-Publikation: 19-Mär-2010
Fakultät: Sonstige Einrichtungen
Fachrichtung: SE - INM Leibniz-Institut für Neue Materialien
Fakultät / Institution:INM
SE - Sonstige Einrichtungen

Dateien zu dieser Ressource:
Datei Beschreibung GrößeFormat 
sm199507.pdf587,02 kBAdobe PDFÖffnen/Anzeigen


Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.