Titel: Optical spectroscopy of Er3+ and Yb3+ co-doped fluoroindate glasses
Verfasser: Ribeiro, C. T.M.
Zanatta, A. R.
Nunes, Luis A. O.
Messaddeq, Younes
Aegerter, Michel A.
Sprache: Englisch
Erscheinungsjahr: 1998
Quelle: Journal of applied physics. - 83. 1998, 4, S. 2256-2260
SWD-Schlagwörter: Optische Spektroskopie
Fluoride
Photolumineszenz
Anti-Stokes-Linie
Aufwärtskonversion
DDC-Sachgruppe: 620 Ingenieurwissenschaften und Maschinenbau
Dokumentart : Journalartikel
Kurzfassung: Optical absorption, Stokes, and anti-Stokes photoluminescence were performed on Er3+-Yb3+ co-doped fluoroindate glasses. For compounds prepared with a fixed 2 mol % ErF3 concentration and YbF3 contents ranging from 0 to 8 mol %, important upconversion processes were observed as a function of temperature and photon excitation energy. Based on the experimental data, two mechanisms for the upconversion (or anti-Stokes photoluminescence) processes were identified and analyzed in detail. At high Yb contents, the upconversion mechanisms are mostly determined by the population of the 2F5/2 levels of Yb3+ ions (or 4I11/2 levels of Er3+ ions, by energy transfer) regardless of the photon excitation energy and temperature of measurement. Moreover, green and red light emission have similar intensities when a large Yb3+ content is present.
Link zu diesem Datensatz: urn:nbn:de:bsz:291-scidok-24864
hdl:20.500.11880/24298
http://dx.doi.org/10.22028/D291-24242
SciDok-Publikation: 3-Dez-2009
Fakultät: Sonstige Einrichtungen
Fachrichtung: SE - INM Leibniz-Institut für Neue Materialien
Fakultät / Institution:INM
SE - Sonstige Einrichtungen

Dateien zu dieser Ressource:
Datei Beschreibung GrößeFormat 
aeg199808.pdf651,93 kBAdobe PDFÖffnen/Anzeigen


Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.