Titel: Influência da textura da cerâmica Ir0.3Ti(0.7-x)PtxO2 na reação de desprendimento de oxigenio
Sonstige Titel: Morphology influence of Ir0.3Ti(0.7-x)PtxO2 ceramic on the oxygen evolution reaction
Verfasser: Da Silva, Luis Antônio
Alves, Valéria Almeida
Da Silva, Marcelo A. Pereira
Aegerter, Michel A.
Sprache: Sonstige
Erscheinungsjahr: 1994
Quelle: Anais / 38° Congresso Brasileiro de Cerâmica; 2° Encontro de Mineradores e Consumidores : [18 a 21 de junho de 1994, Blumenau, SC] / Associação Brasileira de Cerâmica. - Vol. 3. - São Paulo, SP : Associação Brasileira de Cerâmica, 1994, S. 1376-1380
SWD-Schlagwörter: CONDUCTOR
Oxide
Sauerstoff
Rasterelektronenmikroskop
DDC-Sachgruppe: 500 Naturwissenschaften
Dokumentart : InProceedings (Aufsatz / Paper einer Konferenz etc.)
Kurzfassung: -
Films of conductors oxides of nominal composition Ir0.3Ti(0.7-x)PtxO2 (0≤x≤0.7) of 2µm thickness have been prepared from thermal decomposition (400°C) of chloride precursors on metallic Ti support. Their morphology depends strongly on the preparation procedure and has a definitive influence on the behavior of the oxygen evolution reaction (OER). The higher the electrode area, the higher the number of active sites available to the OER. A pre-analysis of these films by Scanning Electron Microscopy (SEM) allows to evaluate the performance of the several ceramic oxide mixtures with respect to the OER. The films containing PtOx, analyzed before and after OER present drastical morphological differences, indicating that this reaction provokes a collapse of the oxide microstructure.
Link zu diesem Datensatz: urn:nbn:de:bsz:291-scidok-23902
hdl:20.500.11880/24243
http://dx.doi.org/10.22028/D291-24187
SciDok-Publikation: 10-Sep-2009
Fakultät: Sonstige Einrichtungen
Fachrichtung: SE - INM Leibniz-Institut für Neue Materialien
Fakultät / Institution:INM
SE - Sonstige Einrichtungen

Dateien zu dieser Ressource:
Datei Beschreibung GrößeFormat 
AEG255.pdf3,06 MBAdobe PDFÖffnen/Anzeigen


Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.