Bitte benutzen Sie diese Referenz, um auf diese Ressource zu verweisen: doi:10.22028/D291-24147
Titel: Characterization of an all solid-state electrochromic window
Verfasser: Tonazzi, Juan Carlos López
Valla, Bruno
Macedo, Marcelo A.
Baudry, Paul
Aegerter, Michel A.
Martins Rodrigues, Ana Candida
Bulhoes, Luis O. S.
Sprache: Englisch
Erscheinungsjahr: 1990
Quelle: Sol-gel optics : 11 - 13 July 1990, San Diego, California / John D. Mackenzie... ed. - Bellingham, Wash. : SPIE, 1990. - (SPIE proceedings series ; 1328), S. 375-390
SWD-Schlagwörter: Cer
Sol-Gel-Verfahren
Titan
Lithium
Elektrolytlösung
Anwendungsschicht
DDC-Sachgruppe: 500 Naturwissenschaften
Dokumentart : InProceedings (Aufsatz / Paper einer Konferenz etc.)
Kurzfassung: Sol-gel cerium - titanium oxide layers present potential application as transparent counter-electrode (ion storage layer) in electrochromic windows and mirrors using lithium conducting electrolyte and WO3 electrochromic coating. The precursor sol, prepared by mixing Ti(OPr1)4 and Ce(NO3)6 (NH4)2 in ethanol, is initially dark red and becomes transparent after a few days aging indicating the presence of Ce3+ complexes. The layers have been obtained by dip coating technique and heat treated at 450°C during 15 minutes. They have been characterized by XRD, SIMS, optical absorption and electrochemical techniques; it is shown that the electrochemical reaction corresponds to a reversible insertion-extraction of lithium ions within a TiO2 amorphous film containing small CeO2 crystallites. At low sweep frequencies the process is controlled by a diffusion mechanism (DLi approximately 6.4 10-12cm2/s at 25°C). Characterizations of an all solid state electrochromic window/glass/ITO/WO3 POE-Li N (SO2 CF3)2/TiO2 - CeO2/ITO/glass/are also presented.
Link zu diesem Datensatz: urn:nbn:de:bsz:291-scidok-23042
hdl:20.500.11880/24203
http://dx.doi.org/10.22028/D291-24147
ISBN der Druckausgabe: 0-8194-0389-X
SciDok-Publikation: 20-Aug-2009
Fakultät: Sonstige Einrichtungen
Fachrichtung: SE - INM Leibniz-Institut für Neue Materialien
Fakultät / Institution:INM
SE - Sonstige Einrichtungen

Dateien zu dieser Ressource:
Datei Beschreibung GrößeFormat 
aeg139.pdf4,99 MBAdobe PDFÖffnen/Anzeigen


Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.