Bitte benutzen Sie diese Referenz, um auf diese Ressource zu verweisen: doi:10.22028/D291-24142
Titel: Electrochromic window with lithium conductive polymer electrolyte
Verfasser: Baudry, Paul
Aegerter, Michel A.
Deroo, Daniel
Valla, Bruno
Sprache: Englisch
Erscheinungsjahr: 1991
Quelle: Journal of the Electrochemical Society. - 138. 1991,2, S. 460-465
SWD-Schlagwörter: Lithium
Lithium-Polymer-Akkumulator
Polymere
Elektrolytlösung
Verdunstung
Elektrode
Röntgenbeugung
DDC-Sachgruppe: 500 Naturwissenschaften
Dokumentart : Journalartikel
Kurzfassung: An electrochromic window was built using WO3 as the electrochromic material and V2O5 as the counterelectrode. Both were deposited onto ITO coated glass panes by vacuum evaporation and were amorphous to X-ray diffraction. The electrolyte was a lithium conducting polymer constituted by a Poly (ethylene oxide) - lithium salt complex. The electrochemical characterization of electrodes was realized by cyclic voltammetry, coulometric titration, and impedance spectroscopy, which allowed the determination of the chemical diffusion coefficients of lithium into WO3 and V2O5. Potentiostatic cycling of the complete transmissive cell yields a transmission variation from 41 to 13% at 633 nm with a response time of 10 seconds at room temperature.
Link zu diesem Datensatz: urn:nbn:de:bsz:291-scidok-22991
hdl:20.500.11880/24198
http://dx.doi.org/10.22028/D291-24142
SciDok-Publikation: 13-Aug-2009
Fakultät: Sonstige Einrichtungen
Fachrichtung: SE - INM Leibniz-Institut für Neue Materialien
Fakultät / Institution:INM
SE - Sonstige Einrichtungen

Dateien zu dieser Ressource:
Datei Beschreibung GrößeFormat 
aeg130.pdf579,17 kBAdobe PDFÖffnen/Anzeigen


Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.