Titel: Estudo de saxs am sóis, géis e vidros de sílica obtidos pelo processo sol-gel
Verfasser: Dos Santos, Dayse Iara
Aegerter, Michel A.
Craievich, Aldo F.
Sprache: Sonstige
Erscheinungsjahr: 1989
Quelle: Cerâmica. - 35. 1989, 229, S. 13-17
SWD-Schlagwörter: Sol-Gel-Verfahren
Röntgen-Kleinwinkelstreuung
Siliciumdioxid
Aerogel
DDC-Sachgruppe: 500 Naturwissenschaften
Dokumentart : Journalartikel
Kurzfassung: -
Systematic SAXS studies have been performed at the LURE Synchrotran, Orsay, using an intense beam of point like cross-section to obtain information about the sol wet gel dried gel silica glass transformation. The intensity curves have been analysed in term of power law in log-log plots, whose exponent is related to mass and surface fractal dimensions of the structure. It was found that almost all phases present fractal structures and for the case of basic gels, is of hierarchical nature. The aerogels are formed by a dense matrix, with a smooth surface and exhibit a very narrow auto-similarity range that gives a mass fractal dimension.
Link zu diesem Datensatz: urn:nbn:de:bsz:291-scidok-22974
hdl:20.500.11880/24197
http://dx.doi.org/10.22028/D291-24141
SciDok-Publikation: 13-Aug-2009
Fakultät: Sonstige Einrichtungen
Fachrichtung: SE - INM Leibniz-Institut für Neue Materialien
Fakultät / Institution:INM
SE - Sonstige Einrichtungen

Dateien zu dieser Ressource:
Datei Beschreibung GrößeFormat 
aeg121.pdf2,48 MBAdobe PDFÖffnen/Anzeigen


Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.