Titel: Electric field effect on the luminescence of KI:Tl
Verfasser: Nouailhat, A.
Perrenoud, R.
Aegerter, Michel A.
Rossel, Jean
Sprache: Englisch
Erscheinungsjahr: 1973
Quelle: Journal of luminescence. - 6.1973, 4, S. 245-255
SWD-Schlagwörter: Thermolumineszenz
Iodide
Thallium
DDC-Sachgruppe: 500 Naturwissenschaften
Dokumentart : Journalartikel
Kurzfassung: Thermoluminescence of KI:Tl, x- or &#946;-irradiated at T<77°K showed 2 main peaks at 105 and 170°K. They are resp. attributed to the recombination of mobile VK centers with Tl0 centers and to the recombination of thermally released electrons from Tl0 centers with Tl2+ centres. Similar experiments performed under static electric fields (E<40 kV cm-1) show that the intensity of the 2nd glow peak is strongly reduced. The relative intensity variation is anticorrelated with the intensity of glow peaks occurring at >230°K. We suggestthat in the temperature range in which Tl0 centres are thermally ionised, the effect of the electric field favour the retrapping of these electrons on other traps (still unknown). Irradiation doses also play an important role and their effects are studied at 77°K and T=200°K.
Link zu diesem Datensatz: urn:nbn:de:bsz:291-scidok-22202
hdl:20.500.11880/24130
http://dx.doi.org/10.22028/D291-24074
SciDok-Publikation: 14-Jul-2009
Fakultät: Sonstige Einrichtungen
Fachrichtung: SE - INM Leibniz-Institut für Neue Materialien
Fakultät / Institution:INM
SE - Sonstige Einrichtungen

Dateien zu dieser Ressource:
Datei Beschreibung GrößeFormat 
aeg027.pdf585,35 kBAdobe PDFÖffnen/Anzeigen


Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.