Titel: 1300-K compressive properties of a reaction milled NiAl-AlN composite
Verfasser: Whittenberger, J. Daniel
Arzt, Eduard
Luton, Michael J.
Sprache: Englisch
Erscheinungsjahr: 1990
Quelle: Intermetallic matrix composites : symposium held April 18 - 20, 1990, San Francisco, California, U.S.A.. - Pittsburgh, Pa. : Materials Research Soc., 1990. - (Materials Research Society symposium proceedings ; 194), S. 211-218
SWD-Schlagwörter: Kristallstruktur
Nickel
Aluminide
Stickstoff
DDC-Sachgruppe: 620 Ingenieurwissenschaften und Maschinenbau
Dokumentart : InProceedings (Aufsatz / Paper einer Konferenz etc.)
Kurzfassung: Cryomilling (high intensity mechanical ball milling in aliquid nitrogen bath) of the B2 crystal structure nickel aluminide leads to a NiAl-AlN composite containing about 10 vol pct second phase which is dispersed as very small diameter (<50 nm) AlN particles in a mantle surrounding particle-free NiAl grains. The AlN particles are the result of reaction milling, where nitrogen incorprated into the matrix during cryomilling reacts with Al during subsequent thermomechanical processing to form a composite. Compressive testing at 1300 K of such materials densified by either hot extrusion or hot isostatic pressing have indicated that strengh at relatively fast strain rates. In addition deformation at 1300 K occurs by two distinct mechanism, where at high strain rates the stress exponent is greater than 13 while at slower rates (<10-7 s-1) a much lower stress exponent (-6) was found.
Link zu diesem Datensatz: urn:nbn:de:bsz:291-scidok-20373
hdl:20.500.11880/24063
http://dx.doi.org/10.22028/D291-24007
SciDok-Publikation: 5-Feb-2009
Fakultät: Sonstige Einrichtungen
Fachrichtung: SE - INM Leibniz-Institut für Neue Materialien
Fakultät / Institution:INM
SE - Sonstige Einrichtungen

Dateien zu dieser Ressource:
Datei Beschreibung GrößeFormat 
ea199011.pdf2,37 MBAdobe PDFÖffnen/Anzeigen


Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.