Titel: Determination of silicate anion constitution in glassy and crystalline lead silicates using an improved TMS technique
Verfasser: Hoebbel, Dagobert
Götz, J.
Vargha, Anna
Wieker, Wolfgang
Sprache: Englisch
Erscheinungsjahr: 1984
Quelle: Journal of non-crystalline solids. - 69. 1984, S. 149-159
SWD-Schlagwörter: Bestimmung
Anion
Silicate
Tetramethylsilan
DDC-Sachgruppe: 540 Chemie
Dokumentart : Journalartikel
Kurzfassung: Using the DMF trimethylsilylation technique developed by Tamás, Sarkar and Roy, the distribution of silicate anions in lead silicate glasses of the composition range PbO·SiO2---4PbO· SiO2 has been reinvestigated. The obtained results agree with earlier findings except for the tetrameric chain anion [SiO4O13]10-, which had not been found before. Crystallization of glassy PbO·SiO2 proceeds via the formation of low-molecular silicate anions [Si2O7]6-, [Si4O13](II)10- and [Si7O22]16-, which characterize the low-temperature crystalline polymorph T---PbO·SiO2. Further heat treatment turns T---PbO·SiO2 into alamosite, characterized by polysilicate chain anions [SiO32-]8.
Link zu diesem Datensatz: urn:nbn:de:bsz:291-scidok-19284
hdl:20.500.11880/23981
http://dx.doi.org/10.22028/D291-23925
SciDok-Publikation: 19-Dez-2008
Fakultät: Sonstige Einrichtungen
Fachrichtung: SE - INM Leibniz-Institut für Neue Materialien
Fakultät / Institution:INM
SE - Sonstige Einrichtungen

Dateien zu dieser Ressource:
Datei Beschreibung GrößeFormat 
hoeb198405.pdf3,79 MBAdobe PDFÖffnen/Anzeigen


Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.