Titel: Silicate groupings in glassy and crystalline 2PbO . SiO2
Verfasser: Götz, J.
Hoebbel, Dagobert
Wieker, Wolfgang
Sprache: Englisch
Erscheinungsjahr: 1976
Quelle: Journal of non-crystalline solids. - 20. 1976, S. 413-425
SWD-Schlagwörter: Silicate
DDC-Sachgruppe: 540 Chemie
Dokumentart : Journalartikel
Kurzfassung: The type and the amount of silicate groupings existing in glassy and crystalline 2PbO·SiO2 have been determined by direct chemical methods: paper chromatography, trimethylsilylation combined with gas-liquid partition chromatography and by the molybdate method. The results obtained by these three different methods are in good agreement and demonstrate, that glassy 2PbO·SiO2 and each of the three main crystalline polymorphs are characterized by its own specific silicate anion distribution: the distribution in vitreous 2PbO·SiO2 is of a polyanionic nature; in T---Pb2SiO4 dimetic groups [Si2O7]6- prevail; M1---Pb2SiO4 contains predominantly [Si4O12]8- rings and H---Pb2SiO4 is a typical polysilicate with chain anions [SiO32-]n. The results fit a structural model according to which glass is a random array of discrete polyatomic groupings; the gradual transition from the glassy state to the stablest crystalline structure is connected with degradation and polymerization of silicate anions.
Link zu diesem Datensatz: urn:nbn:de:bsz:291-scidok-19110
SciDok-Publikation: 9-Dez-2008
Fakultät: Sonstige Einrichtungen
Fachrichtung: SE - INM Leibniz-Institut für Neue Materialien
Fakultät / Institution:INM
SE - Sonstige Einrichtungen

Dateien zu dieser Ressource:
Datei Beschreibung GrößeFormat 
hoeb197605.pdf4,35 MBAdobe PDFÖffnen/Anzeigen

Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.