Titel: On the constitution of silicate groupings in binary lead silicate glasses
Verfasser: Götz, J.
Hoebbel, Dagobert
Wieker, Wolfgang
Sprache: Englisch
Erscheinungsjahr: 1976
Quelle: Journal of non-crystalline solids. - 22. 1976, S. 391-398
SWD-Schlagwörter: Silicate
Gruppierung
DDC-Sachgruppe: 540 Chemie
Dokumentart : Journalartikel
Kurzfassung: Direct chemical methods have been used to determine the type and the percentage of silicate groupings present in binary lead silicate glasses within the composition range 4PbO · SiO2---PbO · SiO2. The results obtained indicate that the constitution and the relative amounts of various silicate groupings change with the changing total amount of SiO2 in the glass. Glasses containing small amounts of SiO2 are characterized by the presence of few low-molecular silicate units; increasing the percentage of SiO2 promotes the formation of higher polymerized silicate groupings. The results are discussed with regard to stoichiometry, and are consistent with Hägg's concept of glassiness.
Link zu diesem Datensatz: urn:nbn:de:bsz:291-scidok-19106
hdl:20.500.11880/23963
http://dx.doi.org/10.22028/D291-23907
SciDok-Publikation: 9-Dez-2008
Fakultät: Sonstige Einrichtungen
Fachrichtung: SE - INM Leibniz-Institut für Neue Materialien
Fakultät / Institution:INM
SE - Sonstige Einrichtungen

Dateien zu dieser Ressource:
Datei Beschreibung GrößeFormat 
hoeb197604.pdf3,83 MBAdobe PDFÖffnen/Anzeigen


Alle Ressourcen in diesem Repository sind urheberrechtlich geschützt.